metal clay, art clay, pmc, bronze clay, copper clay, steel clay
FAQ HomeFAQAsk us a QuestionSave your Favorites
Metal Clay Academy Excellence in Art Clay and Precious Metal Clay PMC
Search Advanced Search
Categories
Beginners (49)
Advanced (14)
Glass (2)
Hollow Forms (1)
Patina and Colours (8)
Stones (8)
Technical (30)
Training (2)
Firing (9)
Finishing (10)
Business (3)
Money saving tips (3)
Search
Advanced Search
FAQs
Search our FAQ to find resolutions to common issues.
What is slip?

Slip is a watered down version of metal clay. You can buy slip or paste directly from the suppliers or make your own by adding water to a small lump of clay, filings or dried out clay. Slip can be used to attach two pieces of metal clay together, fill in small cracks or painted onto leaves, flowers, pods etc to make unique designs.

To make slip from scratch, you need a flat, non-porous surface like a piece of glass or plastic, a palette knife or spatular and some water. Take a small piece of metal clay and add a little water - spritzing it with a spray bottle works well.

Work the water into the clay using the palette knife. When the water is absorbed, add some more. Keep adding water and working it in until the clay forms a thick paste. Put it into a clean container - old style film canisters or small glass jam jars work well. You can add more water to the slip and mix with a plastic stirrer or a paint brush until it's the consistency you want.

Whenever you're filing your leather hard pieces, be sure to collect the filings. These can be added to your slip pot and mixed in.

Clay that has dried out can be reconstituted by cutting or grinding into small pieces and mixing with water. If the dried piece is quite large, you might want to make this into a lump of clay again. Otherwise, you can grind or chop it up and add to your slip pot. Make sure you mix in the ground up pieces very well before using in your designs.


Print  Email  Save  Comments  Notify Me  Delete from Favorites 
Article ID: 10016 Article Created: 06-11-2008 09:40 AM

How well did this article answer your question? 100% 75% 50% 25% 0%

Most Recently Viewed Articles
What is Cubic Zirconia?
A hard and relatively inexpensive synthetic stone, created in laboratories and often cut to resemble a diamond. It is available in a variety of colours and different shapes....
Can I enamel a piece of metal clay which Iíve already tumble polished?
If you want to refire, enamel or solder on a piece of metal clay that has been tumble polished, you may find that moisture has got trapped in the metal. When you heat it again, especially if you heat it fast, the moisture turns to steam and may cause a blister on the surface. You need to dry the piece thoroughly if you have quenched the metal following the initial firing....
What copyright rules are applied to rubber stamps?
Most rubber stamping companies have an Angel Policy. This is a form of Limited License and states how a rubber stamped image may be used - for instance, whether it can be used to create products for sale....
How do I turn slip back into metal clay?
One of the wonderful things about metal clay is that it can be reconstituted back into clay whether it's got too wet - slip - or too dry....
My stone seems to lose its depth and lustre when I put it in a bezel, can I improve the look?
Some stones and also glass cabochons can benefit from having a coloured backing put into the bezel before setting the stone. Opals are particularly good with dark grit emery paper behind them. ...
What are the problems associated with quenching hot metal clay?
If you want to refire, enamel or solder on a piece of metal clay that has been quenched, you may find that moisture has got trapped in the metal. When you heat it again, especially if you heat it fast, the moisture turns to steam and may cause a blister on the surface. You need to dry the piece thoroughly if you have quenched the metal following the initial firing.It is also important to remember that you should not quench a piece which has glass or stones as part of the design. The sudden change in temperature from the firing to the cold water may cause shock and the stone or glass could be damaged or break entirely. Leave your piece to air cool, it should only take a few minutes....
My clay is dry, powdery, flaky and cracking. What can I do?
Spritz or brush the clay with water, wrap it in clingfilm/Saran Wrap and squish the water into the clay. Then leave it for a while. The clay will absorb the water and become usable again. If itís too sticky, leave it open to the air for a short while....
Why is newly fired silver metal clay white?
This is the surface of the silver before burnishing. If you could look at it under a microscope you'd see lots of peaks and valleys. This uneven surface doesn't allow the light to reflect so it appears dull white. ...
Tips and Hints on using UV Resin
The following tips and hints were posted on the Yahoo! Metal Clay Group by Linda at Laughing Girl Arts...
What should I do before I open the packet?
As metal clay begins to dry as soon as you open it, you should be prepared before you open the packet....