Search our FAQ to find resolutions to common issues.
What copyright rules are applied to rubber stamps?

There is a very useful article here about Angel policies. This link also includes rubber stamp companies who have an Angel policy.


Print  Email  Save  Comments  Notify Me  Delete from Favorites 
Article ID: 10072 Article Created: 10-29-2008 17:36 PM

How well did this article answer your question? 100% 75% 50% 25% 0%

Most Recently Viewed Articles
What should I do before I open the packet?
As metal clay begins to dry as soon as you open it, you should be prepared before you open the packet....
How can I publicise my work?
There are a number of very simple ways to publicise your work and raise your profile as a metal clay artist....
What is Cubic Zirconia?
A hard and relatively inexpensive synthetic stone, created in laboratories and often cut to resemble a diamond. It is available in a variety of colours and different shapes....
How do I remove Liver of Sulphur patina from specific areas of my work only?
There are various ways of shining up certain bits of your work after adding a Liver of Sulphur patina. ...
How do I remove enamel from my silver clay piece?
Pam East's book Enameling on Metal Clay: Innovative Jewelry Projects outlines this process. Here Pam gives some basic information to consider....
How can I get a good brass brush effect on very small pieces?
You can buy very small brushes which get into small spaces. Very small burnishing tools also work well to close the pores of the surface of the silver....
My slip is full of animal hairs and other stuff. What can I do?
Depending on how thick the slip is, you can filter it using gauze, muslin or a very fine sieve. Sometimes the lumps in the slip can make an interesting texture although you need to remember that organic material will burn out in the firing....
What is the process for firing Copper clay with Dichroic glass?
The original copper clay (Copprclay or Hadar's clay) that needs to be fired in carbon can't really be combined with glass in one firing. The glass would pick up the carbon during firing . You could design something that allowed you to connect the glass element after the initial firing, like a traditional prong setting.  There are several reasons why Art Clay Copper Clay or Hadar\'s Quick Fire Copper Clay won\'t work with glass. It needs to be fired at a high temperature so the glass would probably liquify too much. Also the Art Clay Copper works best if you put it in a hot kiln so this would crack the glass due to thermal shock. After firing, it has to be dropped into cold water, another reason why it can\'t be used with glass. Question courtesy of Susan Potter...
How thick should my clay be?
This depends on what you are making, how deep the texture you're using is, if you're putting texture on the back and the front and also to some extent personal taste. If you're making a pair of small plain earrings, you can roll the clay out to three cards thick. This should make a light pair of earrings that are strong enough to withstand the wear. If you're using deep texture you should go up to five or six cards thick. Deep texture on the back and front of a piece may require your initial rolling to be even thicker. If your piece is going to get lots of wear, like a pendant with a wrap over bail, the bail part should be a little thicker so it can withstand the wear. You will probably know if you've gone too thin when you try to pick the piece up....
What type of cores can I use to build my metal clay pieces?
Pretty much anything that's combustible and non-toxic can be used as a core to build metal clay pieces. Organic items like snacks, bread, cereal, pasta etc can be used to give support to a piece of work. ...